    Don't laugh: Should I lap PAL6035

    I beleive I'm going to have to lap my PAL6035 because it has some scratches and dark spot on the contact surface. The temps are rather high after I got my replacement CPU since I crushed my first one. There's a strange spot on the surface where it made contact with the TBird die that almost looks like a scortch mark.
    I've never lapped a copper based HS so I'm worried about it. How much will it wear it down? Should I do it or just buy a new one?
    Also, I was considering using auto rubbing compound. Have a friend who used it on his and he said that it worked great on his HS. I have a kind that says it will remove 1500 grit scratches or finer. I'm mentioning this to try remove debris and any air pokets in between.

  2. #2
    Join Date
    Jan 2000
    Location
    massachusettes
    Posts
    622
    Copper will grind down very fast, the smoother the surface the better. Use compound
    instead of paper!! I would think a fine micron grit such as 14.5 particle size should
    be good enough. What do you have to loose if you don't try it, you can always buy another!
    Use a piece of Plate Glass to do the work!
    Oh grind in figure 8 motion! Remember flatter is Better!
    If you cant get some descent grinding compound send me an email and i will deliver
    some to you at cost of shipping only!

    [This message has been edited by Warbird (edited 04-13-2001).]

    [This message has been edited by Warbird (edited 04-13-2001).]

    [This message has been edited by Warbird (edited 04-13-2001).]
    Ford Mustang GT 2001
    281 Cubic Inch/260HP - Fully Loaded - Mach 460 Surround Sound - Silver Metallic - 17" Aluminum Alloy Rims

  3. #3
    Join Date
    Oct 2000
    Location
    Denver, CO
    Posts
    508
    Thanks for the offer Warbird, will keep in mind. I already started off with a 600 grit paper and sure enough the edges are all buffed but the center is barely touched. I'll keep you in mind of I need a good compoud. thanks

  4. #4
    Join Date
    Jul 1999
    Location
    Ontario, Canada
    Posts
    231
    Nothing to laugh at. Lapping the HS will help, but your biggest concern should be getting that heatsink flat against the cpu slug when you mount it. A dark scorched area, high temps and crushed cpu are symptoms of an improperly mounted HS. Ensure you check this out or you will be back to sguare one.

  5. #5
    Join Date
    Sep 2000
    Location
    Grand Junction, CO
    Posts
    767
    If the center is barley touched you are probably not keeping it flat enough while you lap. Try to put some pressure in the exact center of the HS.

    I like to lap in one direction for a while and then in one direction 90 degrees from the first. I think it is easier to check for flatness and to see when a finer grit has removed all scratches from the previous grit that way. Maybe do the final polishing with a figure eight

    You can get wet or dry paper up to 2,000 grit at most auto parts stores.

    Good luck with it, Bill

    ------------------
    Duron 700@969 & PAL6035
    MSI K7T Turbo, 256MB Kingmax PC150
    IBM 75GXP, 7,200 RPM, 20Gig HD
    Fong-Kai FK603 case & 275W PC Cooling PS
    Matrox G-450 & Iiyama Pro 17
    Mitsumi 48X CD & 250 internal Zip
    Linksys 10/100 Ethernet
    Win 98 SE
    AMD 9950 Quaad-core processor
    M2N-SLI Deluxe board
    4 GB OCZ Gold
    WD 500GB SATA2 HD
    Antec True Power 750
    Antec Sonta case
    BFG 8600GT 256MB video
    Samsung 940bx 19" LCD
    Samsung SH-S203B DVD
    On board NIC
    SB Audigy sound
    XP Pro 64 bit

  6. #6
    ol' man is offline workin fingas to the bone
    Join Date
    Oct 2000
    Posts
    9,664
    I say only do the polish in a linear motion. My experience is that anytime you start going in circles you are going to make it round instead of flat. When you go in a linear motion(ie back and forth or side to side) it should take down the same amount all around. I have used 1500 grit sand paper to do this and stuck it to my counter top with water. A good super fine sharpening stone would be good also. I like the plate glass idea for final polish though. Never thought of that one.I have done this to three different heatsinks. At first I did the circular motion and that caused it too be round instead of flat. I question but I may be wrong about the figure 8 motion doing the same. For a final light polish though as has been stated a figure 8 should be fine but a linear still might be best. Good luck.

    ------------------
    800e@960mhz cBO_Sl1
    abit BE6-II
    256mb pc 133 2.2.2.
    32mb gf2-mx dual display
    Sparkle 300watt psu
    win2k
    100mb zipper
    52xcd-rom

  7. #7
    Join Date
    Jan 2000
    Location
    Stornoway, Isle of Lewis, Scotland
    Posts
    1,215
    I lapped my 6035 using 250 grit all the way to 800 grit and it resulted in a 2C temp drop

    ------------------
    Duron 700@1100 2.1v Air Cooled
    ALPHA PAL6035 & Delta 7000rpm
    Abit KT7 Raid w/voltage mod
    IBM 75 GXP UDMA100
    Gainward Geforce2 Pro 64Meg
    256Mb Crucial PC133 CAS2
    Belinea 10-30-40 17" 0.26
    Turtle Beach Santa Cruz S/Card
    ASUS 50x
    Mitsumi 8x 2x CD-R
    GlobalWin 802 w/5x80mm YS-Techs
    Duron 700@1100 2.1v Air Cooled - RIP

  8. #8
    Join Date
    Sep 2000
    Location
    chicago Il. usa
    Posts
    377
    What I've read of other's posts, they are all right to an extent. Use a flat surface(I use a good mirror)start coarser grits(500)in a back and forth at 90 degree to each other(straight cuts and at 90 to each other will remove more material)Once you have the sink flat you will want to do your final polishing in a circular or figure 8 motion(1500-2000) If ya use a rubbing compound be sure to clean it very well before application of AS or whatever thermal goop you'll use. Or you can use AS when you sand. When done you should have mirror like finish with a clean reflection(no waves) Have fun

    ------------------
    Cel. 566 @ 994
    Alpha PAL 6035 w/Delta Black Label
    BX6 rev.2
    128 meg Kingmax pc150
    30.7 Gb MaxPlus 40 ATA 66 7200rpm
    GeForce 2 MX
    Awe 64
    56K Conexant PCI
    300 W PSU
    Cel. 566 @ 1054 max 38c
    MSI 6905 Master ver2
    Alpha PAL 6035 w/Delta Black Label
    BX6 rev.2

  9. #9
    Join Date
    Oct 2000
    Location
    Denver, CO
    Posts
    508
    Interesting luta. Is the purpose of useing AS while sanding to make sure no other material gets in the heatsink?

  10. #10
    Join Date
    Jan 2000
    Location
    massachusettes
    Posts
    622
    Interesting comments, A Figure 8/Linear motion probably will make no difference. If the work surface is either convex/concave the piece will always come out the opposite. Since the only area involved here is about
    1/2x1/4 its not really necessary to get the whole HS flat. Just the center!! But it is important not to include any type of scratches/digs on the surfaces!

    ------------------
    P3700@840
    BE6-II/Micron 256MB ECC
    GeForce II GTS
    IBM 20GB ATA66
    SB Live
    BA Digital Media Theater Speakers
    48X Mitsumi CD-ROM
    Hitachi 17" SuperScan
    Plextor 12/10/32 CD-RW
    Ford Mustang GT 2001
    281 Cubic Inch/260HP - Fully Loaded - Mach 460 Surround Sound - Silver Metallic - 17" Aluminum Alloy Rims

Thread Information

Users Browsing this Thread

There are currently 1 users browsing this thread. (0 members and 1 guests)

Posting Permissions

  • You may not post new threads
  • You may not post replies
  • You may not post attachments
  • You may not edit your posts
  •